Rust Stop primer

Name: Rust Stop primer
Brand: Würth
SKU: 0890191

PRIM-RUSTSTOP-750ML

Art.-no. 0890191

EAN 4060053866554

All versions

Individual price display after login

Rust Stop primer

Art.-no. 0890191

Individual price display after login

Quantity

Exclusively for trade customers

Login/Register
Call customer service: +632 584 4619

Brushable, active corrosion protection for metallic surfaces

Excellent corrosion protection

Meets corrosion category C3 "high" in accordance with DIN EN ISO 12944.

Approx. 500 h in accordance with DIN EN ISO 9227.

Resistant to water, sea water and many chemicals.

Quick drying

Treated materials are quickly ready for use and transportation.

Ideal as a transport coating in steel construction.

Can be painted over

Short-term temperature resistance up to +120 °C

VOC-compliant

Reduced solvent content.

Complies with the maximum VOC content specified in the VOC Directive (1999/13/EC).

Notice

Note: Can be painted over with standard top-coat paint systems as per the table (see technical data sheet).

Application area

The usage instructions are recommendations based on the tests we have conducted and are based on our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

Product information

Würth Catalogue

Datasheets(X)

Safety data sheet

Certificates/ Documents

Application area

Corrosion protection primer for use in automotive construction, shipbuilding, metal and steel construction, tool manufacturing, bridge construction, tank construction, pipeline construction, container construction, agriculture and forestry, municipal management, construction machinery etc.

Instructions

The surface must be clean, dry and free of grease. Remove loose rust, paint and dirt using a wire brush, scraper or similar tool. Stir well before use. Apply 2 coatings approx. 1 hour apart. Recommended nozzle size 1.6 mm.

Weight of content	960 g
Contents	750 ml
Chemical basis	Alkyd resin
Colour	Red brown
Drying time	16 h
Yield (area)	8 m²
Min. application quantity in volume/area	90 ml/m²
Max. processing temperature	25 °C
Density	1.28 g/cm³
Min./max. temperature resistance	-30 to 80 °C
Max. temperature resistance	80 °C
Max. short-term temperature resistance	120 °C
Density conditions	at 20°C
Min. processing temperature	15 °C
Shelf life from production	12 Month
Conditions to maintain shelf life from production	at 10°C to 35°C, no exposure to sunlight, no heat sources

Paint system	1-8 hours	9-20 hours	1 day	2 days	3 days
Synthetic resin	+	-	+	+	+
2C top coat	+	-	+	+	+
2C filler	+	-	-	-	+
1C acrylate	+	-	-	+	+
Adhesion primer	+	-	-	-	+
NitroCombi	+	-	-	-	+

Suitable glove:

Product

Description

Nitrile chemical protective glove

Description:

Permeation level: 2

With cotton velour finish inside.

Nitrile chemical protective glove long, heavy-duty design

Description:

Permeation level: 3

Chemical protective glove chloroprene

Description:

Permeation level: 1

Heavy-duty design

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time

Permeation level

< 10 min

≥ 10 min

≥ 30 min

≥ 60 min

≥ 120 min

≥ 240 min

≥ 480 min

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.